The effect of hydration layers on the anodic growth and on the dielectric properties of Al2O3 for electrolytic capacitors
2014
Hydrous films were grown on high purity and cubicity Al foils for electrolytic capacitors in deionized water, ethylene glycol - deionized water and in glycerol - deionized water for different immersion times. According to the X-ray diffraction patterns the hydration treatment allowed to grow a pseudo boehmite layer on Al surface whose morphology is appreciably affected by the bath composition. Capacitance measurements and photoelectrochemical findings suggest that a more compact barrier layer forms during the immersion in alcohol containing solutions. The hydration in water allowed to save energy and to prepare more blocking oxide films. The beneficial effect of hydration in hot water on th…
Kinetic of growth and physico-chemical characterization of anodic films on magnesium
2008
Photoelectrochemical monitoring of rouging and de-rouging on AISI 316L
2017
Electrochemical conditions for inducing rouging on surface of AISI 316L in quasi neutral aqueous solution are studied. Potentiostatic polarization at 0.6 V vs. SSC at pH ∼ 7 allowed growth of colourless passive films with a band gap slightly lower than that estimated for the oxide grown on the SS surface by air exposure due to chromium dissolution. Under stronger anodic polarization (UE = 1.5 V vs. SSC) coloured passive films are formed, mainly constituted by iron oxide according to their band gap (Eg = 2.0 eV). Etching in citric acid at 60 °C results to be effective in removing rouging.
Photoelectrochemical evidence of inhomogeneous composition at nm length scale of anodic films on valve metals alloys
2016
Abstract Anodic films of different thickness (∼30 nm and 70 nm) were grown by anodizing sputtering-deposited Ta-19at% Al to different formation voltages. N incorporation into the anodic films was inducing by performing the anodizing process in ammonium containing solutions. Layered anodic films were prepared by a double formation procedure with a first anodizing step in ammonium biborate solution and second anodizing step in borate buffer solution, or vice versa. Glow Discharge Optical Emission Spectroscopy was employed to show the distribution of N across the oxide. Photoelectrochemical measurements evidenced a red shift of the light absorption threshold due to N incorporation. A model was…
Electrochemically-induced TiO2 incorporation for enhancing corrosion and tribocorrosion resistance of PEO coating on 7075 Al alloy
2018
Abstract 7075 Al alloy was PEO-treated in a silicate based electrolyte containing 3 g l-1 potassium titanyl oxalate using unipolar and bipolar pulsed current waveforms. The coating formed by the bipolar waveform with the wider cathodic pulses showed volcano-like surface morphology with no evidence of large pores at the metal/coating interface. It revealed the highest corrosion performance due to the synergistic effect of TiO2 incorporation and structural/morphological features along with a better passivation behavior indicating no pitting susceptibility. For this coating, the tribocorrosion tests showed no potential drop during sliding under 1 N with the lowest volume loss of 0.022 mm3.
Formation of anodic films on sputtering-deposited Al–Hf alloys
2009
Abstract The growth of barrier-type anodic films at high efficiency on a range of sputtering-deposited Al–Hf alloys, containing from 1 to 95 at.% Hf, has been investigated in ammonium pentaborate electrolyte. The alloys encompassed nanocrystalline and amorphous structures, the latter being produced for alloys containing from 26 to 61 at.% Hf. Except at the highest hafnium content, the films were amorphous and contained units of HfO 2 and Al 2 O 3 distributed relatively uniformly through the film thickness. Boron species were confined to outer regions of the films. The boron distributions suggest that the cation transport number decreases progressively with increasing hafnium concentration i…
The influence of surface treatment on the anodizing of magnesium in alkaline solution
2011
Abstract The mechanism of magnesium anodizing after mechanical polishing or HF pickling was studied. X-ray Photoelectron Spectroscopy and Photocurrent Spectroscopy were employed to characterize both the initial films formed on Mg soon after surface treatments and the anodic films grown in strongly alkaline solutions. Electrochemical and capacitance measurements were performed in order to study the oxidation process and to check if the kinetic of growth fits the Mott–Cabrera high field model. From Tafel plots it was possible to estimate the activation distance, while the simulation of the barrier layer growth as a function of the potential at high scan rate allowed to estimate the other kine…
Photoelectrochemical characterization of amorphous anodic films on Ti-6at.%Si
2013
Abstract The solid state properties of anodic films grown galvanostatically on sputtering-deposited Ti–6at.%Si alloys were studied as a function of the formation voltage (5–40 V). From the photocurrent spectra a band gap of ∼3.4 eV was estimated for all the investigated thicknesses, which is almost coincident with the value measured for amorphous TiO 2 . The photocharacteristics allowed to estimate the flat band potential of the films, which resulted to be more anodic for thicker layers and allowed to evidence a change from n-type semiconducting material to insulator by increasing the formation voltage. A dielectric constant of ∼31 was estimated by differential capacitance measurements. The…